Abstract
This study investigated the evolution process of high-volume slag cement (HVSC) paste from a chemo-mechanical standpoint. HVSC specimens with a 70 w.t. % slag replacement rate were studied at various ages. Evolution of phase assemblage, microstructure development, and micromechanical properties were analyzed using TGA/XRD/MIP/SEM-EDS and nano-/micro-indentation techniques. A two-scale micromechanical model was built to predict the effective elastic modulus based on the nanoindentation results. Key findings include: 1) Between 7 and 28 days, the formation of calcium silicate hydrate (C-S-H) gel phase improves the effective elastic modulus by filling capillary pores; 2) From 28 to 90 days, the phase assemblage and microstructure remain stable, with a transition from low-density to high-density C-S-H; 3) Between 90 days and 2 years, slag rims produced by slag grains result in increased elastic modulus; 4) The two-scale micromechanical model, combined with nanoindentation data, accurately predicts the effective modulus of HVSC composites, although the unhydrated slag grains-hydrated cement matrix interface may cause an overestimation at an early age. With longer curing time, this interface disappears owing to the continuous hydration of large slag particles and therefore a good match is found between the modelling and experimental results.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.