Abstract
A new type of in-situ composite nano-multilayer plate with ultra-high strength (b 2112 MPa), Q235 steel plate with nano-layered structure of lath martensite produced by severe cold-rolling, was developed. After cold-rolling, subsequent annealing has great effect on the deformed lath morphology and grain refinement. Microstructure recrystallizing course have taken place after long time annealing at 350 °C. The recrystallization activation energy is 151 kJmol-1. Microstructure characteristics along rolling direction arrangement was decreased after annealing at 400 °C. In addition to the ultrafine ferrite grains, nano-carbides precipitated uniformly in the specimen annealed at 500 °C. Annealing at and above 600 °C resulted in coarse ferrite grains with spheroidized coarse carbides, causing grain growth. The average crystal size is about 4.7 m after annealing for 60 min at 600 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.