Abstract
Three kinds of brass-plated steel cords with different brass-plating amounts from 2.62 to 5.01 g/kg were prepared and their adhesion properties to rubber compounds were studied. Adhesion properties decreased with the increase in the brass-plating amount from 2.62 to 3.88 g/kg. Furthermore as the increase of brass-plating amount over 3.88%, adhesion property increased. The strong adhesion of brass-plated steel cord with low brass-plating amount to the rubber was shown not only after curing but also after hostile aging treatments. The good adhesion stability against humidity aging of adhesion property for brass-plated steel cord with low brass-plating amount to rubber compound was discussed in terms of the formation and growth of adhesion interphase determined by AES depth profile. The good adhesion stability of brass-plated cord with low brass-plating amount can be resulted from the suppression of the excessive growth of copper sulfide and the inhibition of dezincification due to the low brass-plating amount.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.