The platelike bainitic ferrite growth rates were calculated by two modified diffusional models. Good agreements between experimental and theoretical results are found in Fe-0.59C wt.%, Fe-0.81C wt.% and Fe-0.478C-4.87Ni wt.% alloys. A slowing down effect due to the alloying element Mo is emphasized in Fe-0.69C-1.8Ni-0.8Mo wt.% alloy. However, the experimental data are lower than theoretical ones about two orders in Fe-C-8.7Ni wt.% alloys. According to the discussion of the results, it is suggested that the bainite transformation mechanism may relates to steel composition and transformation temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.