Abstract
The grazing incidence diffraction (GID) method in side inclination mode, described by Ma et al. in 2002, of polycrystalline thin-film residual stress was revisited and explained using simple geometric relations. To overcome the issue of decreasing peak intensity of this method, which is induced by the decreasing incident angle because of the Eulerian cradle Chi-tilt, an improvement of Omega (ω)–Phi (φ) compensation was devised and applied to a NiFe thin-film sample. The geometry of this improved ω–φ compensated GID method in side inclination mode is detailed in this paper. This improvement guarantees a constant incident angle on the sample surface and a fixed sample illumination volume during measurement. The measured data were analysed using parametric refinement in DIFFRAC.TOPAS v6 software in Launch Mode, and details of the input file (.INP) are explained in this paper. The tensile stress of the NiFe thin-film sample was measured to be 1181 ± 85 MPa using this improved method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.