Abstract
Dynamic ferrite transformation behavior was investigated over a wide temperature range using a 6Ni–0.1C steel. Softening in flow stress due to dynamic transformation was observed at temperatures above Ae3, the ortho-equilibrium austenite-to-ferrite transformation temperature. Microstructural observation revealed that ferrite grains formed at temperatures above Ae3 showed deformation microstructures, and those grains were reversely transformed to austenite during subsequent holding at the same temperature. Therefore, we concluded that dynamic ferrite transformation could certainly occur even above Ae3.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.