Abstract
An Al–Cu–Li aerospace alloy has been investigated to determine the order in which corrosion at different types of sites occurs in AA2099-T83. Specifically, the sequence of galvanic attack on intermetallic (IM) particles and other sites of AA2099-T83 was determined as a function of time, in 0.1 M NaCl, through the use of scanning electron microscopy and electron backscatter diffraction characterization techniques. The earliest attack occurred at isolated grains and grain boundaries and on Li-containing dispersoids. Similarly, some constituent IM particles showed evidence of trenching in the surrounding alloy matrix. These IM particles included Al7Cu2Fe and another group of unidentified particles which displayed complete trenching within the first 10 min of exposure. Al13(Fe, Mn)4 were next most active followed by Al37Fe12Cu2 with Al6(Fe,Mn) and large TiB2 particles being the least active.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.