Abstract
AbstractDomain structure and growth mechanism of PbTiO3 thin films were investigated using a transmission electron microscopy(TEM) from the viewpoint of size effects. At initial growth stage of (111)-oriented PbTiO3 films prepared by metalorganic chemical vapor deposition(MOCVD), triangle-shaped islands were grown on Pt(111)/SiO2/Si before becoming a continuous film. Triangular islands grew gradually in a lateral dimension. This means that PbTiO3 films grew two-dimensionally at initial growth stage. In cross-sectional TEM photomicrographs, (101)-twin boundaries (90° domain walls) and inclination of {110} or {101}-plane were observed in PbTiO3 islands. This result indicates that such small PbTiO3 islands have a tetragonal structure and could have spontaneous polarization. The minimum island which had 90° domain walls was 10nm high and 18nm wide.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.