Abstract
A room temperature ferromagnetic Fe doped ZnO bulk sample has been synthesized by co-doping 2 at% Mn with 2 at% Fe in ZnO. The final firing temperature for the preparation of the Zn0.96Mn0.02Fe0.02O sample is the same as the final firing temperature for the preparation of the Zn0.98Mn0.02O sample and in this case it is found to be 490 °C. It has been found that room temperature ferromagnetism in Zn0.96Mn0.02Fe0.02O is a factor of 1.6 times more than that observed in Zn0.98Mn0.02O samples. The size of the saturation magnetic field for the Zn0.96Mn0.02Fe0.02O sample is, however, only a factor of 7 times more than that observed for nanocrystalline undoped ZnO.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.