Abstract
The Mn-oxide/SrTiO3 photoelectrode for oxygen evolution reaction was investigated by in-situ Mn K-edge XAFS spectroscopy under UV irradiation. The oxidization of the Mn oxide was observed via photoexcited carrier transfer, which results in the positive potential shift of the Mn oxide cocatalyst toward oxygen evolution reaction. Introduction Photoelectrochemical water splitting is a candidate for the sustainable production of hydrogen gas using solar energy.1 Recently, MnO x have been shown to remarkably improve the photoelectrochemical activity for water splitting, because the MnO x on the semiconductors work as an efficient oxygen evolution cocatalyst.2 Thus, the surface modification of MnO x cocatalysts to a semiconductor photoelectrode is presently attracting attention as an efficient photoelectrochemical system for water splitting. However, the photoexcited carrier transfer processes at the photocatalyst/cocatalyst interface are not fully understood. In this study, photoexcited carrier transfer toward the MnO x cocatalyst from a SrTiO3 photoelectrode was investigated by in-situ Mn K-edge XAFS spectroscopy under UV irradiation (Fig. 1). Experimental n-Type SrTiO3 substrates were used after photodeposition of the Mn oxide cocatalysts, according to a previous work.2 The surface morphology of the MnO x cocatalysts was observed by scanning electron microscopy (SEM), confirming that the MnO x thin film was deposited on the SrTiO3 surface. A Teflon electrochemical cell was equipped with a Pt wire counter electrode and a Ag/AgCl (saturated KCl) reference electrode in 0.1 M Na2SO4aqueous solution with Ar bubbling. The in-situ XAFS measurements were performed at BL-12C of the Photon Factory and BL01B1 of SPring-8 as fluorescence excitation spectra using 19 element Ge detectors. XAFS spectra of the prepared samples were measured at various potentials under dark conditions or under UV irradiation using a Xe lamp.3 Results and discussion First,the in-situ XAFS measurements of the MnO x /SrTiO3 photoelectrode were tested at 0.5 V under UV irradiation (Fig. 2). The peak position at 6557.8 eV was gradually shifted to 6560.0 eV under irradiation, which suggests that the Mn3+ species changed to Mn4+ due to the migration of photoexcited holes, which is consistent with the photoelectrochemical reaction where the Mn oxide species acts as an oxygen evolution cocatalyst via the transfer of photoexcited holes. On the other hand, when the XAFS spectra were taken for the applied potential at 0.0 V or -0.5 V, the peak position shifted to 6559.2 eV or 6557.8 eV, respectively, indicating that the potential shift of MnO x via the photoexcited hole transfers from photoelectrode to MnO x cocatalyst is dependent on the applied electrode potential. These results demonstrate that the photoexcited carrier transfer into the cocatalyst from the photoelectrode can be probed under UV irradiation by in situ electrochemical XAFS measurement. References (1) Nocera, D. G. Acc. Chem. Res. 2012, 45, 767-776.(2) Wang, D.; Li, R.; Zhu, J.; Shi, J.; Han, J.; Zong, X.; Li, C. J. Phys. Chem. C 2012, 116, 5082-5089.(3) Yoshida, M.; Yomogida, T.; Mineo, T.; Nitta, K.; Kato, K.; Masuda, T.; Nitani, H.; Abe, H.; Takakusagi, S.; Uruga, T.; Asakura, K.; Uosaki, K.; Kondoh, H. Chem. Commun. 2013, 49, 7848-7850.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.