Abstract
Radial ball bearings made of metal, ceramics and plastics are commonly used as important components in various types of industrial machinery. Due to the latest markets demands for elements capable of withstanding e.g. corrosive environment, metallic bearings are being gradually replaced by components produced from high performance engineering plastic polymers. In order to investigate the failure mechanism of polymer bearings and further improve their performance in practical applications in an underwater environment, in this research crack propagation in Poly-ether-ether-ketone (PEEK) was studied by rolling contact fatigue (RCF) testing under water. Crack propagation in the inner ring raceway surface and subsurface areas of PEEK bearings after testing was observed by a laser confocal microscope. Cracks and flaking failure were found on the bearing raceway surface. From the RCF tests results, it was found that the detected cracks could be divided into three groups: Main Surface Cracks, Semi-circular Cracks and Main Subsurface Cracks. It is concluded that flaking occurs on the inner ring raceway due to the fusion of semi-circular cracks and a main subsurface crack.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.