Abstract
The paper deals with the issue of coating and surface finishing with edge preparation prior to the coating. Nanocomposite AlCrSiN hard coatings were deposited on WC-Co substrates with a negative substrate bias voltage in range of-80 to-120 V using cathodic arc evaporation system. The effect of variation in the bias voltage on the coating-substrate adhesion and nanohardness was investigated. The maximum nanohardness of coating was 37.7 ± 1.5 GPa with the good coating-substrate adhesion. Static Mercedes indentation test was performed on a Rockwell-type hardness tester. The indents were studied by scanning electron microscope to evaluate the coating-substrate adhesion. The H to E ratio that represents resistance to the plastic deformation was determined. The influence of surface roughness and time of used surface finishing methods on the coating-substrate adhesion was also investigated.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call