Numerical investigation of the reactor pressure vessel behaviour under severe accident conditions taking into account the combined processes of the vessel creep and the molten pool natural convection

Abstract

Analysis of the WWER lower head behaviour and its failure has been performed for several molten pool structures and internal overpressure levels in a reactor pressure vessel (RPV). The different types of the molten pools (homogeneous, conventionally homogeneous, conventionally stratified, stratified) cover the bounding scenarios during a hypothetical severe accident. The parametric investigations of the failure mode and RPV behaviour for various molten pool types, its heights and internal overpressure levels are presented herein. A coupled treatment in this investigation includes: (i) a 2-D thermohydraulic analysis of a molten pool natural convection. Domestic NARAUFEM code has been used in this detailed analysis for prediction of the heat flux from the molten pool to the RPV inner surface; and (ii) a detailed 3-D transient thermal analysis of the RPV lower head. Domestic 3-D ASHTER-VVR finite element code has been used for the numerical simulations of the high temperature creep and failure of the lower head. The effect of an external RPV cooling, temperature-dependent physical properties of the molten pool and vessel steel, the hydrostatic forces and vessel dead-weight were taken into account in this study. The obtained results show that lower head failure occurs as a result of the vessel creep process which is significantly dependent on both an internal overpressure level and the type of molten pool structure. In particular, it was found that there were combinations of ‘overpressure-molten pool structure’ when the vessel failure started at the ‘hot’ layers of the vessel. It was shown in this study that the processes in the molten pools reach a quasistationary state at 2000…3000 s after molten pool formation. Numerical results in this paper illustrate that the large creep deformations of the vessel lower head can lead to an appearance of the gaps between the vessel surface and the molten pool crust. It is obvious that the joint thermal and structural analyses are needed for the accurate tracing of the initial bounds of the vessel and molten pool during simulations.