Abstract
Plasticity effects on fatigue growth were simulated for a physically short crack. The material description comprised the Drucker-Prager yield surface, non-associated flow rule and non-linear combined hardening. The simulated development of the growth limiting parameter agreed with the experimental crack behaviour with early rapid propagation followed by a transition to slow R-controlled growth. The crack was open to the tip without any crack face closure throughout all load cycles. Instead compressive residual stresses developed at the unloaded tip which supplied an explanation to the slow rate of the propagated short crack in this bainitic high strength bearing steel. The material’s strength differential effect was the key difference explaining why compressive residual stresses instead of crack face closure was responsible for the short crack effect in this material.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.