Abstract
The thermal-metallurgical model of primary γ gamma phase through couple of heat transfer model, dendrite selection model, columnar/equiaxed transition (CET) model, multicomponent dendrite growth model and nonequilibrium solidification model is further developed on the basis of criteria of minimum growth velocity, constitutional undercooling and marginal stability of planar front during nickel-based single-crystal weld pool solidification. It is clearly indicated that crystallographic orientation plays more important role than heat input in microstructure development and solidification behavior. The dendrite trunk spacing and solidification temperature range along the solid/liquid interface are symmetrically distributed about the weld pool centerline in (001) and [100] welding configuration, while they are asymmetrically distributed in (001) and [110] welding configuration. The dendrite size and solidification temperature range are beneficially smaller in (001) and [100] welding configuration than that of (001) and [110] welding configuration regardless of heat input. The mechanism of asymmetrical solidification cracking because of crystallography-dependent growth kinetics and solidification behavior is proposed. Optimum low heat input (low laser power and high welding speed) refines dendrite size and suppresses the solidification temperature range to minimize the solidification cracking susceptibility and ameliorate the weldability through microstructure control, while high heat input (high laser power and low welding speed) deteriorates the weldability and weld integrity. It is therefore imperative to optimize the welding conditions for successful defect-free laser welding. Moreover, the promising theoretical predictions agree well with the experiment results. The useful model is also applicable to other single-crystal superalloys with similar metallurgical properties by laser welding or laser cladding, and provide a more accurate and reliable way of solidification cracking susceptibility evaluation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.