Abstract
The growth kinetics of CdSe nanocrystals nucleated from TOPSe and cadmium oleate were investigated in octadecene, a non-coordinating solvent. The effects of temperature and the oleic acid concentration on the kinetics of both nucleation and particle growth were investigated. It was found that increasing oleic acid concentrations led to smaller numbers of nuclei, smaller initial nuclei size, and larger final particle sizes. The rate constant for steady-state CdSe deposition was found to be 2.2 × 10-6 cm s-1 at ≈ 265 °C, far slower than the diffusion limit. The number of growing particles remained constant following the initial nucleation step. The radius of the primary CdSe nuclei varied from 1.0 ± 0.1 nm down to 0.8 ± 0.2 nm at lower oleic acid concentrations. Between 2 and 8% of the available Cd was consumed during nucleation. From the residual TOPSe and cadmium oleate concentrations at the onset of Ostwald ripening, the solubility of 2.2 nm CdSe in octadecene is measured to be 6.4 × 10-5 M2 at 265 °C. T...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.