Nucleated Poly(l-lactic acid) with N, N′-oxalyl bis(benzoic acid) dihydrazide

Abstract

One of the major challenges in the field of Poly(l-lactic acid) (PLLA) is the enhancement of crystallization. In the present work, the evaluation of the influence of N, N′-oxalyl bis(benzoic acid) dihydrazide (TBOD), as a novel organic nucleating agent, on the non-isothermal crystallization, melting behavior, and thermal stability of PLLA was performed using differential scanning calorimeter and thermogravimetric analysis. Non-isothermal crystallization measurement revealed that TBOD had an excellent accelerating effect for the crystallization of PLLA in cooling, and upon the addition of 3 wt% TBOD, PLLA exhibited the highest onset crystallization temperature and the crystallization peak temperature, as well as the largest non-isothermal crystallization enthalpy. In particular, when the TBOD concentration was 1 wt% ∼ 3 wt%, the onset crystallization temperatures were higher than the theoretical ceiling temperature of crystallization, thoroughly demonstrating the powerful crystallization promoting ability of TBOD. Additionally, the non-isothermal crystallization behavior of PLLA/TBOD depended on the TBOD concentration, cooling rate as well as the final melting temperature. The melting behavior of PLLA/TBOD after non-isothermal crystallization further confirmed the effect of TBOD on the crystallization process and crystal structure of PLLA, and the appearance of the double melting peaks during melting stages was attribute to the melting-recrystallization. For melting behavior after isothermal crystallization, the crystallization temperature and crystallization time significantly affected the melting behavior of PLLA/TBOD. The addition of TBOD could not change the thermal decomposition profile of the PLLA, but the thermal stability did not regularly decrease with increasing of TBOD concentration, indicating that there might exist intermolecular interaction between PLLA and TBOD.