Abstract
Superconducting (Bi,Pb) 2Sr 2Ca 2Cu 3O y /Ag tapes are doped with uranium compounds to introduce flux pinning defects from neutron-induced fission. The composition and distribution of elements in cross sections of the tapes were probed with a scanned 3 MeV proton microbeam using proton induced X-ray emission (PIXE). Distributions of the constituent elements were found to be heterogeneous on a scale of 10 μm. By combining the PIXE analysis with Rutherford backscattering spectrometry, the stoichiometry of the superconductor within the tape was measured, including oxygen from elastic scattering, revealing a departure from the desired 2223 composition. In one of the tapes, PIXE elemental maps of the Ag distribution showed diffusion of Ag into the superconductor from the enclosing jacket. Crystals of the same material, not fabricated into tapes, did not contain the contaminants and had a more ideal stoichiometry. Correlation maps between the constituent elements, deduced from the elemental maps, indicate the presence of secondary or unreacted phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.