Abstract
Pt-based catalysts are commonly employed as NOx-trapping catalysts for automobiles, while perovskite oxides have received attention as Pt-free NOx-trapping catalysts. However, the NOx storage performance of perovskite catalysts is significantly inferior at low temperatures and with coexisting gases such as H2O, CO2, and SO2. This study demonstrates that NOx storage reactions proceed over redox site (Mn, Fe, and Co)-doped SrTiO3 perovskites. Among the examined catalysts, Mn-doped SrTiO3 exhibited the highest NOx storage capacity (NSC) and showed a high NSC even at a low temperature of 323 K. Moreover, the high NOx storage performance of Mn-doped SrTiO3 was retained in the presence of poisoning gases (H2O, CO2, and SO2). NO oxidation experiments revealed that the NSC of Co-doped SrTiO3 was dependent on the NO oxidation activity from NO to NO2 via lattice oxygen, which resulted in an inferior NSC at low temperatures. On the other hand, Mn-doped SrTiO3 successfully adsorbed NO molecules onto its surface at 323 K without the NO oxidation process using lattice oxygens. This unique adsorption behavior of Mn-doped SrTiO3 was concluded to be responsible for the high NSC in the presence of poisoning gases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.