Abstract
Select mechanical, thermal, and rheological properties of star-blocks consisting of 5–21 polystyrene-b-polyisobutylene (PSt-b-PIB) arms radiating from cyclosiloxane cores are described. The tensile properties of products containing 23–41 wt % of PSt are substantially higher (9.6–23.8 MPa) than those of linear triblocks of comparable arm molecular weights and compositions over the 25–85°C temperature range. The mechanical properties of star-blocks seem to be much less sensitive to diblock contamination than linear triblock thermoplastic elastomers of similar hard/soft segment composition. The tensile strength of star-blocks increases by increasing the number of arms (Nw,arm) and reaches a plateau in the Nw,arm = 5–10 range. Star-blocks exhibit higher strengths with lower PSt segmental Mn than linear triblocks. Solvent cast triblock copolymers exhibit higher tensile strengths than compression molded products; however, star-blocks show no significant property differences between cast and molded samples. The dynamic melt viscosities of the star-blocks are substantially lower than those of linear triblocks with comparable hard/soft segment compositions, which is consistent with the star's unique microarchitecture and should lead to improved overall processibility. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 815–824, 1999
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Polymer Science Part A: Polymer Chemistry
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.