Abstract
We present a new material design concept, silicon quantum dot (Si QD) polymers, for which surface-functionalized Si QDs can be regarded as a large monomer in the polymers. As a prototypical example, vinyl-functionalized Si QDs, i.e., divinylbenzene-capped Si QDs (DVB-Si QDs) synthesized by adopting divinylbenzene (DVB) capping molecule to the hydride-terminated Si QD (H-Si QD) via Pt-catalyzed hydrosilylation was introduced and polymerized with a styrene monomer to yield Si QD–polystyrene (Si QD–PS) polymers. To demonstrate controllability of the content of Si QDs in the polymers as in conventional polymers, three Si QD content varied Si QD–PS polymers were systematically prepared, named as Si QD–PS-A, Si QD–PS-B, and Si QD–PS-C. It has been demonstrated that the content of the Si QDs in the Si QD–PS polymers was well controlled by the amount of the DVB-Si QD used, as found to be 3.8 wt% (Si QD–PS-A), 10.0 wt% (Si QD–PS-B), 20.0 wt% (Si QD–PS-A), and 37.4 wt% (DVB-Si QD), which was deduced from TGA results. Thin films of the Si QD–PS polymers and the freestanding DVB-Si QDs were successfully fabricated by a spin-coating method and it was found that the refractive index of the thin films dried at 40 °C was linearly increased as the content of the Si QD in the polymers was increased from 1.586 (0 wt%), to 1.590 (3.8 wt%), to 1.592 (10.0 wt%), to 1.592 (20.0 wt%), and to 1.614 (37.4 wt%).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.