Abstract
The nanostructured 0.9LiMn0.9Fe0.1PO4·0.1Na3V2(PO4)2F3/C composites are successfully synthesized by a facile solvothermal method followed by mechanical activation and subsequent carbonthermal reduction process. Behaviours of bi-phase co-existence and element mutual-substitution have been investigated by XRD, TEM/EDX and FTIR. The result shows that the composites have dual phase boundaries including the semi-coherent phase interface and incoherent phase interface, as well as the advantage of Na3V2(PO4)2F3 acting as ionic conductor. Due to the multifunctional phase and (Mn,Fe)-V mutual doping as well as nano-carbon continual conducting network, enhanced Li+ migration and charge transfer of nano-hybrid is obtained. Compared with pristine one, the 0.9LiMn0.9Fe0.1PO4·0.1Na3V2(PO4)2F3/C composites exhibit high rate capability and cycling ability, showing 125.5, 106.4 mAh g−1 at 1.0 C, 3.0 C at room temperature, respectively, with high capacity retention up to 93.9% after 600th at 2 C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.