Abstract
A novel surface treatment for the MlNi3.8Co0.75Mn0.4Al0.2 (La-rich mischmetal) hydrogen storage alloy has been carried out by using an aqueous solution of HF and KF with a little addition of KBH4. The results of scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) showed that rough surface was formed and Al was partly dissolved into the solution after the treatment. The result of XPS indicated the formation of Ni3B and LaF3 compounds on the alloy surface by the treatment. The probable chemical reaction mechanism for the surface treatment was introduced. The treatment resulted in significant improvements in the activation property, discharge capacity and cycle life of the alloy, especially the high rate dischargeability (HRD). The HRD of the treated alloy still remained 54.9% while that of the untreated one was only 15.1% at a discharge current density of 1200 mA/g.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.