Abstract
LaMnO 3+δ nanocrystals with a mean diameter of 75 A, were synthesized using SBA-15 mesoporous silica. The magnetic properties of the nanocrystals showed a novel size effect and were quite different from those of bulk crystal. The magnetic and electron spin resonance measurement results indicate that the existence of two transition temperatures, 278 and 235 K, which are higher than Neel and Curie temperature of bulk LaMnO 3+δ . The ESR spectrum was observed even at the lower transition temperature and consisted of the two broad lines whose shape changed at each transition temperature. The magnetization curve at 77 K was well reproduced by the summation of the two superparamagnetic magnetizations corresponding to antiferromagnetic and ferromagnetic nanoparticles, respectively. These results suggest that there are noninteracting ferromagnetic and antiferromagnetic nanoparticles with transition temperatures of 278 and 235 K, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.