Novel Sandwich-Structured Flexible Composite Films with Enhanced Piezoelectric Performance.

Abstract

Piezoelectric poly(vinylidene fluoride) (PVDF) and its copolymers have been widely investigated for applications in wearable electric devices and sensing systems, owing to their intrinsic piezoelectricity and superior flexibility. However, their weak piezoelectricity poses major challenges for practical applications. To overcome these challenges, we propose a two-step synthesis approach to fabricate sandwich-structured piezoelectric films (BaTiO3@PDA/PVDF/BaTiO3@PDA) with significantly enhanced ferroelectric and piezoelectric properties. As compared to pristine PVDF films or conventional 0-3 composite films, a maximum polarization (Pmax) of 11.24 μC/cm2, a remanent polarization (Pr) of 5.83 μC/cm2, and an enhanced piezoelectric coefficient (d33 ∼ 14.6 pC/N) were achieved. Simulation and experimental results have demonstrated that the sandwich structure enhances the ability of composite films to withstand higher poling electric fields in comparison with 0-3 composites. The sandwich-structured piezoelectric films are further integrated into a wireless sensor system with a high force sensitivity of 288 mV/N, demonstrating great potential for movement monitoring applications. This facile approach shows great promise for the large-scale production of composite films with remarkable flexibility, ferroelectricity, and piezoelectricity for wearable sensing devices.