Abstract
Sodium acrylate (NaAA) and acrylamide (AM) were grafted onto poly (vinyl alcohol) (PVA) using potassium persulfate as an initiator, Graft copolymerization namely poly (vinyl alcohol)-g-poly (acrylamide/sodium acrylate) (PVA-g-PAM/SAC). The poly (vinyl alcohol)-g-poly (vinylamine/sodium acrylate) (PVAMC) was prepraed by Hofmann rearrangement.The PVAMC homogeneous membrane was characterized by fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM).The water resistance of the PVAMC membranes is the best when pH of the PVAMC solutions was 4, at that time the numbers of-NH3+ and-COO- groups trended to be equal, so the isoelectric point was pH=4. At 90 °C the pervaporation of PVAMC composite membrane was tested and showed that the separation factor and the permeate flux were about 1001 and 1341 g/(m2·h) for 90wt% ethanol aqueous solution, and they were about 1297 and 1040 g/(m2·h) for 90wt% isopropanol aqueous solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.