Abstract
The phenolic content in lignin makes it a potential substitute for formaldehyde-based synthetic wood adhesives. In the present work, lignin isolated from Hevea brasiliensis was treated with laccase enzyme to obtain active lignin. The activated lignin (NaOH treated) was further formulated with natural rubber latex (NR-latex) to prepare bio-adhesive. Complementary analysis such as modulus of rupture (MoR), modules of elasticity (MoE), internal bonding (IB), Fourier transform infrared (FTIR) spectroscopy, thickness swelling (TS), and scanning electron microscopy (SEM) were applied to characterize a medium density fibre-board (MDF) prepared based on bio-adhesive formulation. It was found that bio-adhesive formulation of 10 g NR-latex with 10 g of lignin has the highest MoR of 16 MPa, while the formulation of 15 g NR-latex with 5 g lignin showed the highest MoE of 15 MPa. The TS result showed that there is a weight gain on MDFs with a lower proportion of NR-latex content which consequently increases the density of the composites. The FTIR analysis of formulated bio-adhesive revealed the significant difference in chemical composition with different proportions of lignin and NR-latex in bio-adhesive. Finally, SEM examination of the interfaces of formulated bio-adhesive and wood fibre material showed the better dispersion with no adhesive lumps.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.