Abstract
A co-precipitation method was used for processing chitosan (CHI)/calcium hydrogen phosphate dehydrate (DCPD) hybrid material. CHI solution was mixed into 1.0-M calcium nitrate solution. CHI/DCPD hybrid material was prepared by the above explained addition of CHI and Ca ion source to 1.0-M diammonium hydrogen phosphate solution. It was observed by transmission electron microscopy that CHI and DCPD were mixed within submicron meter scale. CHI/HA bulk materials derived from the CHI/DCPD hybrid materials were obtained by using a hydrothermal hot-pressing (HHP) method. A pressure of 40MPa was initially applied to the sample. An HHP autoclave was heated up to 150°C for 2h. Modified 3-point bending tests were conducted to obtain an easy estimate of the fracture toughness for the CHI/HA bulk materials made with the HHP method. The critical stress intensity factor Kc of the fabricated CHI/HA bulk materials was enhanced from 0.30 to 0.40MPam1/2 by the hybridization of CHI into DCPD.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.