Abstract
AbstractMethyl‐tri(phenylethynyl)silane (MTPES) was successfully synthesized by the reaction of lithium phenylacetylide with methyltrichlorosilane. The structure was characterized by HRMS, FTIR, 1H‐NMR, 13C‐NMR, 29Si‐NMR, and elementary analysis. Thermal cure process was monitored by DSC, DMA, and FTIR. MTPES was heated to free flowing liquid around 130°C and thermally polymerized at 327–377°C to form thermoset. Thermal and oxidative properties were evaluated by TGA analysis. Thermoset exhibits extremely high heat‐resistance and TGA curve in nitrogen shows the temperature of 5% weight loss (Td5) of 695°C and total weight loss at 800°C of 7.1%. TGA shows a high Td5 of 565°C even in air, although the total weight loss at 800°C was 56.1% of the initial weight, much higher than that in nitrogen. The high heat resistance of MTPES was ascribed to crosslinking reaction concerning ethynyl groups. Aging studies performed at elevated temperatures in air on a thermoset showed that MTPES is oxidatively stable to 300°C. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 2488–2492, 2006
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.