Abstract
Normal sintering of Li‐doped and Li/Ta‐codoped potassium sodium niobate (KNbO3–NaNbO3, KNN)‐based ceramics was investigated to clarify the optimal sintering condition for densification, microstructure, and electrical properties. It was found that density increased greatly within a narrow temperature range but tended to decrease when the sintering temperature slightly exceeded the optimal one, accompanied by the appearance of abnormal grain growth, which was considered to be due to the intensified volatilization of alkali metal oxides. Piezoelectric and dielectric properties also showed a similar relationship between the density and sintering temperature, but the highest piezoelectric strain coefficients were obtained at the temperatures lower than that for the highest density, because both densification and composition affect the electrical properties. The highest d33 value of 206 pC/N was obtained for the Li‐ and Ta‐codoped KNN ceramics prepared at 1090°C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.