Abstract
The nonlinear current-voltage and dielectric properties of (Al3++Ta5+) co-doped TiO2 (ATTO) ceramics are represented. Microstructural analysis reveals that sintered ceramics are highly dense and nonporous. ATTO ceramics exhibit low loss tangent (tanδ<0.1) and large dielectric permittivity (ε′˜103-104). Furthermore, ATTO ceramics exhibited nonlinear current-voltage characteristics. The best dielectric properties are achieved in the (Al1/2Ta1/2)0.05Ti0.95O2 ceramic with a very low tanδ (˜0.012) and high ε′ (˜104) with excellent dielectric-temperature stability with a temperature coefficient at 150 °C as low as 2.69%. The resistivity of insulating phases decreases with increasing Al3+ and Ta5+ concentrations, which is correlated to decreased breakdown voltage. The nonlinear electrical properties and dielectric response are explained based on the electrical response of internal interfaces.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.