Abstract
A single-step synthesis of magnesium ferrite (MgFe2O4) nanoparticles with an average crystallite size of about 8.5 nm synthesized via mechanochemical processing of binary oxide precursors at room temperature is reported. The study highlights the nature of the cation disorder and of the spin arrangement in mechanosynthesized MgFe2O4 as well as its response to changes in temperature. An unusual property of the magnetization enhancement in nanoscale mechanosynthesized MgFe2O4 is reported. Whereas the inner core of a MgFe2O4 nanoparticle exhibits a partly inverse spinel structure with a Néel type collinear spin alignment, the major features of the ionic and spin configurations in the grain boundary (surface) region are a nonequilibrium cation distribution and a canted spin arrangement. Although the spin-canting effect tends to reduce the magnetic moment, the magnetization enhancement exhibited by mechanosynthesized MgFe2O4 is attributed to the nearly random distribution of magnetic cations in the surface regions of nanoparticles. On heating above 623 K, the mechanosynthesized MgFe2O4 relaxes to a structural and magnetic state that is similar to the bulk one.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.