Abstract
ABSTRACTThe growth conditions of A-plane AlN and GaN epitaxial layers by radio-frequency plasma assisted molecular beam epitaxy on R-plane sapphire substrates were investigated. The growth temperature and V/III supply ratio dependency on structural quality and surface roughness was described. The optimum V/III ratio for A-plane GaN and AlN layers was shifted to nitrogen rich side compared to the C-plane layers. A-plane GaN/AlN superlattices (SLs) were also grown on R-plane sapphire substrates. The X-ray diffraction peaks from a primary and a 1st satellite were observed. From a comparison of low temperature photoluminescence peak wavelength between A-plane and C-plane SLs, the built-in electrostatic field originated from spontaneous and piezoelectric polarization is negligible for A-plane SLs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.