A knowledge of the distribution of cross-link densities (CDs) in the constituent rubber phases of an elastomer blend is essential to understand its overall service properties, but phase-resolved CD estimations have so far been limited to qualitative assessments. In a first study of its kind, we demonstrate a phase-resolved quantification of the CDs in sulfur-cured blends of natural rubber (NR) and styrene–butadiene rubber (SBR) using solid-state ¹H homonuclear dipolar double-quantum (DQ) magic-angle spinning (MAS) NMR spectroscopy. The blends were also subjected to prolonged thermo-oxidative aging to monitor the chemical changes in the two phases. Analyses of the residual dipolar coupling constant (Dᵣₑₛ), arising due to spatial restrictions by cross-links to molecular motions, as observed in MAS and static ¹H DQ experiments, suggest that unaged NR and SBR cross-link to similar extents. A minimum in Dᵣₑₛ after around 500 h of aging duration is observed in NR, associated with the formation of highly mobile defect fractions, as seen from free induction decay (FID) combined with transverse relaxometry, with further cross-linking up to 1000 h. SBR appears more stable, with a gradual increase in Dᵣₑₛ over the aging duration. Phase-resolved experiments reveal a somewhat less cross-linked SBR phase in an unaged 50:50 blend. The phase-specific distribution of CDs in the blend phases becomes significant upon aging, which suggests that NR ages more strongly in the blend as compared to the aged single vulcanisates, thus dictating the blend properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.