Nitrogen-Atom Bonding at SiO2/Si Interfaces in Metalinsulator-Semiconductor (MIS) Stacked Gates Made by Integration of Plasma Assisted Oxidation-Deposition and Rapid Thermal Processing

Abstract

ABSTRACTSiO2 thin films were deposited by remote PECVD on Si surfaces exposed to species generated in O2/N2 and O2/NH3 plasmas. The surface chemistry was studied by Auger Electron Spectroscopy, AES, and the electrical properties of the SiO2/Si interface by high frequency and quasi-static Capacitance-Voltage, C-V, measurements. The AES results showed that Ccontamination was removed by exposure to both plasma-excited gas mixtures, but that N-atoms were incorporated into the SiO2 film, and Si-N bonds were formed at the SiO2/Si interface. C-V measurements indicated that the Si-N bonding structure, rather than the N-atom concentration, is critical in determining the interface electrical properties. The effects of Rapid Thermal Annealing, RTA, on the electrical properties of these SiO2/Si interfaces were also studied.