Abstract
High performance, high solid and low in volatile organic content (VOC) multifunctional coatings have wide applications in protection and decoration of materials. This work describes the synthesis of novel hyperbranched polymer (HBP) based polyurethanes (PUs) that exhibit antimicrobial property and are environmentally benign. Nitrogen rich HBP having nitrogen atom as a core was synthesized by A3 + B3 polycondensation in two step reaction. In the first step, monomer A3, a tricarboxylic acid, was synthesized by triethanolamine (B3, the core) with succinic anhydride, while in the second step, monomers A3 and B3 were used to synthesize hyperbranched polyester polyol by polycondensation reaction. The HBP thus formed was reacted with 4,4′-methylenedicyclohexyl diisocyanate (H12 MDI) in varying ratios of NCO to OH to form NCO- terminated PU prepolymers in a self-catalyzed reaction. The prepolymers were then coated onto mild steel panels as well as tin foils and stored at ambient conditions for 20 days to evaluate the moisture-cured PU-urea film properties. The formation of tribasic acid (A3), HBP and PU was confirmed by 1H NMR, 13C NMR, FTIR and ESI-mass spectroscopy. Thermal, mechanical, anti-corrosive and antimicrobial studies as well as the effect of varying NCO to OH ratio on these properties were investigated. The properties of PU-urea were found to be suitable for corrosion protection as well as biomedical and various other applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.