Abstract
The indium-tin-oxide [ITO(80 nm)] and Ni(5 nm)-Au(10 nm) films were separately deposited on glass substrates, p-GaN layers, n/sup +/-InGaN-GaN short-period-superlattice (SPS) structures, and nitride-based light-emitting diodes (LEDs). It was found that ITO on n/sup +/-SPS structure could provide us an extremely high transparency (i.e., 93.2% at 465 nm) and also a reasonably small specific contact resistance of 1.6/spl times/10/sup -3//spl Omega//spl middot/cm/sup 2/. Although the forward voltage which corresponds to 20-mA operating current for LED with ITO on n/sup +/-SPS upper contact was slightly higher than that of the LED with Ni-Au on n/sup +/-SPS upper contact, a 30% higher output intensity could still be achieved by using ITO on n/sup +/-SPS upper contact. Moreover, the output power of packaged LED with ITO was about twice as large as that of the other conventional Ni-Au LEDs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.