Nitric oxide-releasing vascular grafts: A therapeutic strategy to promote angiogenic activity and endothelium regeneration

Abstract

Small-diameter vascular grafts (SDVGs) are associated with a high incidence of failure due to infection and obstruction. Although several vascular grafts are commercially available, specific anatomical differences of defect sites require patient-based design and fabrication. Design and fabrication of such custom-tailored grafts are possible with 3d-printing technology. The aim of this study is to develop 3d-printed SDVGs with a nitric oxide (NO)-releasing coating to improve the success rate of implantation. The SDVGs were printed from polylactic acid and coated with blending of 10 wt% S-nitroso-N-acetyl-D-penicillamine into the polymeric substrate consisting of poly (ethylene glycol) and polycaprolactone. Our results show that NO is released in the physiological range (0.5–4 × 10−10 mol·cm−2·min−1) for 14 days and NO-releasing coating showed significant antibacterial potential against Gram-positive and Gram-negative strains. It was shown that both NO-releasing and control grafts are biocompatible in-vitro and in-vivo. Interestingly, the NO-releasing SDVGs dramatically enhanced ECs proliferation and significantly enhanced ECs migration in-vitro compared to control grafts. In addition, the NO-releasing SDVGs showed angiogenic potential in-vivo which can further prove the results of our in-vitro study. These findings are expected to facilitate tissue regeneration and integration of custom-made vascular implants with enhanced clinical success. Statement of significanceA series of 3d-printed small-diameter vascular grafts (SDVGs, <6 mm) with controlled release of nitric oxide (NO) were prepared to combine the advantages of 3D printing technology and NO-releasing systems. The resulting NO-releasing grafts were promisingly showing sustained NO release in the physiological range over a two weeks period. In addition to the evaluation of endothelial cell migration in-vitro, we implanted for the first time the NO-releasing vascular grafts in a chick chorioallantoic membrane (CAM) to investigate the effect of the prepared grafts on the angiogenesis in-vivo. The fabricated grafts also exhibited bactericidal properties which prevent the formation of a biofilm layer and can thereby enhance the chance of endothelialization on the surface. Taken together, the innovative combination of rapid and highly accurate 3d-printing technology as a patient-specific fabrication method with NO-releasing coating represents a promising approach to develop bactericidal SDVGs with improved endothelialization.