Abstract
Pt-doped Ni (NiPt) silicide agglomeration in terms of NiSi crystal orientation, Pt segregation at the NiSi/Si interface, and residual stress is studied for the first time. In the annealing of Ni monosilicide (NiSi), the growth of NiSi grains whose NiSi b-axes are aligned normal to Si(001) [NiSi(010) ∥ Si(001)] with increasing Pt segregation at the NiSi/Si interface owing to a high annealing temperature was observed. The residual stress in NiSi(010) ∥ Si(001) grains also increases with increasing annealing temperature. Furthermore, the recrystallization of NiSi(010) ∥ Si(001) grains with increasing residual stress continues through additional annealing after NiSi formation. After the annealing of NiSi(010) ∥ Si(001) grains with their strain at approximately 2%, the start of NiPt silicide agglomerates accompanied by stress relaxation was observed. This preferential recrystallization of NiSi(010) ∥ Si(001) grains with increasing residual stress is considered to enhance the NiPt silicide agglomeration.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call