Nickel substitution induced effects on gas sensing properties of cobalt ferrite nanoparticles

Abstract

Ni2+ ion induced unusual conductivity reversal and an enhancement in the gas sensing properties of ferrites based gas sensors, is reported. The Co1−xNixFe2O4 (for x = 0, 0.5 and 1) nanoparticles were synthesized by wet chemical co-precipitation method and gas sensing properties were studied as a function of composition and temperature. The structural, morphological and microstructural characterization revealed crystallite size of in the range 10–20 nm with porous morphology consisting of nano-sized grains. The Energy Dispersive X-ray (EDX) mapping confirms homogeneous distribution of Co, Ni, Fe and O elements in the ferrites. The non-stoichiometry of the inverse spinel type ferrites and the relative concentration of Ni3+/Co3+ defects were studied using X-ray photoelectron spectroscopy. It is found that the addition of Ni2+ ions into cobalt ferrite shows preferred selectivity towards CO gas at high temperature (325 °C) and ethanol gas at low temperature (250 °C), unlike undoped cobalt ferrite or undoped nickel ferrite, which show similar response for both these gases. Moreover, an unusual conductivity reversal is observed, except cobalt ferrite due to the difference in reactivity of the gases as well as characteristic non-stoichiometry of ferrites. This behavior is highly gas ambient dependent and hence can be well-exploited for selective detection of gases.