Abstract
ABSTRACTReactions between Ni and amorphous carbon (a-C) below 600°C have been investigated using differential scanning calorimetry (DSC) and in situ annealing in a transmission electron microscopy (TEM) of Ni/a-C layered films deposited by DC sputtering. DSC data show that there are two exothermic peaks in the temperature range around 200-600°C. One is a weak and broad peak below 500°C and the other is a strong and sharp peak at around 530°C. In situ heating in the TEM revealed that the low temperature peak corresponds to a series of reactions for nickel carbide (Ni3C) formation and decomposition into Ni and carbon, most likely in a glassy state. The higher temperature peak was found to correspond to graphitization of a-C by a solution-precipitation mechanism. Graphite formed in this process is strongly textured with the (0002) graphite basal planes parallel to the original Ni/a-C interface.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.