Abstract
A layer of Ni-Cr-Si-B-Fe alloy was successfully coated on plain steel substrate by hot dipping process. The Ni-Cr-Si-B-Fe alloy coating has a homogeneous thickness of 3mm. The chemical composition and microstructure were studied with SEM and XRD in this paper. The result shows that the Ni-Cr-Si-B-Fe alloy coating is defect-free and chemical bonded with plain steel substrate. A light band zone of 8-10 m width is between Ni-Cr-Si-B-Fe alloy coating and plain steel substrate, and may be considered as a quickly solidified layer. The coating microstructure is a heterogeneous microstructure and changes from the light band zone to the surface of the coating, which is composed mainly of coarse columnar dendrite, needle-like precipitates and scattered eutectic structures. Four regions across the thickness of Ni brazing alloy coating, due to solidification conditions upon hot-dipping, have been identified with distinguished microstructure. In γ-(Fe, Ni) solid solution matrix, the hard phases of CrB, Fe2B and Cr23C6 is identified in the coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.