Abstract
This research studies on VUV/O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -treated aromatic polyurea film from near-edge X-ray absorption fine structure (NEXAFS) and X-ray photoelectron spectroscopy (XPS) spectra. These spectra indicate that the benzene ring was cleaved after the treatment, and carboxyl and hydroxyl groups were formed at the cleaved sites. The VUV/O <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">3</sub> -treated polyurea was applied to polymethylmethacrylate (PMMA) microchip for microchip electrophoresis (MCE) of bovine serum albumin (BSA). Fast electroosmotic mobility of 4.6×10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-4</sup> cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> V <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> s <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> was realized as well as reduction of the BSA adhesion. This functional surface is useful for high speed MCE analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.