Abstract
The tensile stress–strain behavior and fracture properties of some new soybean oil based polymeric materials were investigated at room temperature. These materials were prepared by the cationic copolymerization of regular soybean oil, low saturation soybean oil (LoSatSoy oil), or conjugated LoSatSoy oil with styrene and the diene comonomers divinylbenzene, norbornadiene, or dicyclopentadiene in a process initiated by boron trifluoride diethyl etherate (BF3 · OEt2) or related modified initiators. These new polymeric materials exhibited tensile stress–strain behavior ranging from soft rubbers through ductile to relatively brittle plastics. The Young's moduli of these polymers varied from 3 to 615 MPa, the ultimate tensile strengths varied from 0.3 to 21 MPa, and the elongation at break varied from 1.6 to 300%. These properties are obviously related to their crosslink densities. The conjugated LoSatSoy oil polymers had higher mechanical properties than the corresponding LoSatSoy oil and regular soybean oil polymers with the same stoichiometry. Some conjugated LoSatSoy oil polymers with appropriate stoichiometries showed yielding behavior in the tensile test process. A variety of new polymer materials can thus be prepared by varying the stoichiometry, the type of soybean oil, and the crosslinking agent. These soybean oil based polymers possessed mechanical properties comparable to those of commercially available rubbery materials and conventional plastics and thus may serve as replacements in many applications. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 60–77, 2001
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.