A new processing technique for preparing hyroxyapatite (HAp) ceramics has been developed using the hydrothermal hot‐pressing (HHP) method. Powder mixed dibasic calcium phosphate dihydrate and calcium hydroxide mixed with a Ca/P ratio of 1.67 was treated at 150°C and 40 MPa. The HHP method with the selection of the powder enabled the HAp to be solidified at the low temperature. The resulting HAp ceramics had a tensile strength of approximately 10 MPa. Furthermore, the HAp ceramics possessed a lamellar microstructure and high porosity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.