Abstract
New Pb-based 1212 layered cuprates containing sulfur have been synthesized in the (Pb0.75S0.25) Sr2 (Y1−xCax) Cu2Oz system. X-ray diffraction analysis shows that the almost single-phase samples are obtained within a region of 0.0≤x≤0.5. The crystal structure of each sample has a tetragonal symmetry with the typical lattice constants a=0.3837 nm and c=1.186 nm. As Ca content x is increasing, the semiconductor-like behavior is suppressed. But after only annealing under ambient O2 pressure, none of the samples show any trace of superconductivity. On the other hand, when the samples are annealed under high O2 pressure of about 13.6 MPa, they show resistivity dropping phenomenon in a region of 0.5≤x≤0.7. Among them, the lowest resistivity sample with x=0.6 has an onset temperature of the resistivity dropping at about 22.5 K. Moreover, this sample shows a diamagnetic signal at about 21.5 K. These phenomena are attributed to superconductivity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call