Abstract
The perovskite-type oxide La2−xSrxNiO4 (x=1/8) was prepared by a new precursor route. The reaction proceeds in the self-ignition mode. Single-phase powder and gas-tight ceramic samples can be produced by single annealing of decomposition products. It was shown that as a result of thermobaric treatment of La2−xSrxNiO4 (x=1/8) the solid solution La2−xSrxNiO4 with a higher concentration of strontium and the second phase La3Ni2O7 are formed. Short-term (5min) thermobaric treatment (P=2.5GPa) at t°=900°С changes the unit cell parameters, but is not accompanied by structural transitions. At the same time, morphological restructuring of the sample occurs—the agglomerates delaminate into thin plates crystals. It was established that the permittivity of the material exposed to thermobaric treatment is much higher compared to that of the sample annealed at atmospheric pressure and virtually does not depend on frequency in a wide temperature range.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.