New aramid‐based nanocomposites: Synthesis and characterization

Abstract

AbstractNew type of nanocomposites containing various proportions of montmorillonite in aromatic polyamide was prepared via solution intercalation method. Aramid chains were synthesized by reacting 4,4′‐oxydianiline with isophthaloyl chloride in N,N′‐dimethyl acetamide. Dodecylamine was used as swelling agent to change the hydrophilic nature of montmorillonite into organophilic. Appropriate amounts of organoclay were mixed in the polymer solution using high‐speed mixer for complete dispersion of the clay. Thin films cast from these materials after evaporating the solvent were characterized by XRD, TEM, mechanical, thermal, and water absorption measurements. The structure and morphology of the nanocomposites determined by XRD and TEM revealed the formation of exfoliated and intercalated clay platelets in the aramid matrix. Mechanical data indicated improvement in the tensile strength and modulus of the nanocomposites with clay loading up to 6 wt%. The glass transition temperature increased up to 12 wt% clay content and thermal stability amplified with increasing clay loading. The water absorption reduced gradually as a function of organoclay and approached to zero with 20 wt% organoclay in the aramid. POLYM. ENG. SCI., 2008. © 2008 Society of Plastics Engineers