Abstract
Abstract Neutron diffraction measurements were used to obtain a better understanding of the ageing behaviour in dual-phase ferrite + martensite steels. Therefore, the influence of different ageing treatments on the tempering of low-alloyed 0.4 and 0.7% C FeMnCrMo-martensite and 0.1% C FeMnCrMo dual-phase steels was investigated. On tempering at 170 and 350°C, the sequential precipitation of η- and θ-carbides, as well as the loss of tetragonality was observed in the martensite. The decrease in austenite lattice parameter after tempering is due to stress relaxation in the material. These observations offer an acceptable explanation for the large yield stress increase after ageing at 170°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.