Abstract

Abstract The REMn 0.5 Ni 0.5 O 3 (RE = La, Nd) and YMn 0.5 Co 0.5 O 3 compounds, prepared by solid-state reaction under air, were investigated by X-ray diffraction (XRD) and neutron powder diffraction (NPD). The La-compound contains some lanthanum vacancies decreasing the lattice parameters and increasing the crystal distortion. Nearly stoichiometric compositions were found for the other compounds prepared under similar conditions. The NPD data of all compounds indicate some ordering of the mixed transition ions over the octahedral site, since the crystal structure is better described in monoclinic space group P 2 1 / n that accounts for two distinguishable octahedral sites, rather than in orthorhombic Pbnm . Such results contrast with those obtained from X-ray diffraction where the mixed ions appear to be randomly distributed over the only octahedral site of the Pbnm space group. The low-temperature NPD patterns of YMn 0.5 Co 0.5 O 3 exhibit some magnetic peaks, below 70 K. The magnetic structure at 1.4 K consists of two collinear ferromagnetic sublayers with saturated magnetic moments of 3.26(2) μ B and 2.14(2) μ B per ion, at the 2 c - and 2 d -site, respectively. The low-temperature NPD patterns of LaMn 0.5 Ni 0.5 O 3 and NdMn 0.5 Ni 0.5 O 3 exhibit an obvious increase in intensity over the only nuclear peak, at 2 θ ∼ 36.89° and 36.40°, respectively. Although such behavior indicates a ferromagnetic ordering, the magnetic structure could not be refined because of the faint magnetic properties, more likely due to the incomplete atomic ordering.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.